![Template:Infobox element/symbol-to-top-image/alt](https://upload.wikimedia.org/wikipedia/commons/thumb/3/38/Hf-crystal_bar.jpg/220px-Hf-crystal_bar.jpg) |
Hafnium |
---|
Pronunciation | (HAF-nee-əm) |
---|
Appearance | steel gray |
---|
Standard atomic weight Ar, std(Hf) | 7002178490000000000♠178.49(2)[1] |
---|
Hafnium in the periodic cairt |
---|
|
Zr ↑ Hf ↓ Rf
|
lutetium ← hafnium → tantalum
|
| |
Atomic nummer (Z) | 72 |
---|
Group | group 4 |
---|
Period | period 6 |
---|
Block | d-block |
---|
Element category | Transeetion metal |
---|
Electron confeeguration | [Xe] 4f14 5d2 6s2 |
---|
Electrons per shell | 2, 8, 18, 32, 10, 2 |
---|
Pheesical properties |
---|
Phase at STP | solit |
---|
Meltin pynt | 2506 K (2233 °C, 4051 °F) |
---|
Bylin pynt | 4876 K (4603 °C, 8317 °F) |
---|
Density (near r.t.) | 13.31 g/cm3 |
---|
when liquid (at m.p.) | 12 g/cm3 |
---|
Heat o fusion | 27.2 kJ/mol |
---|
Heat o vapourisation | 571 kJ/mol |
---|
Molar heat capacity | 25.73 J/(mol·K) |
---|
Vapour pressur
P (Pa)
|
1
|
10
|
100
|
1 k
|
10 k
|
100 k
|
at T (K)
|
2689
|
2954
|
3277
|
3679
|
4194
|
4876
|
|
Atomic properties |
---|
Oxidation states | −2, +1, +2, +3, +4 (an amphoteric oxide) |
---|
Electronegativity | Pauling scale: 1.3 |
---|
Atomic radius | empirical: 159 pm |
---|
Covalent radius | 175±10 pm |
---|
Colour lines in a spectral rangeSpectral lines o hafnium |
Ither properties |
---|
Naitural occurrence | primordial |
---|
Creestal structur | hexagonal close-packed (hcp) |
---|
Speed o soond thin rod | 3010 m/s (at 20 °C) |
---|
Thermal expansion | 5.9 µm/(m·K) (at 25 °C) |
---|
Thermal conductivity | 23.0 W/(m·K) |
---|
Electrical resistivity | 331 n Ω·m (at 20 °C) |
---|
Magnetic orderin | paramagnetic[2] |
---|
Young's modulus | 78 GPa |
---|
Shear modulus | 30 GPa |
---|
Bulk modulus | 110 GPa |
---|
Poisson ratio | 0.37 |
---|
Mohs haurdness | 5.5 |
---|
Vickers haurdness | 1760 MPa |
---|
Brinell haurdness | 1700 MPa |
---|
CAS Nummer | 7440-58-6 |
---|
History |
---|
Prediction | Dmitri Mendeleev (1869) |
---|
Diskivery | Dirk Coster an George de Hevesy (1922) |
---|
First isolation | Dirk Coster an George de Hevesy (1922) |
---|
Main isotopes o hafnium |
---|
Isotope
|
Abundance
|
Hauf-life (t1/2)
|
Decay mode
|
Product
|
172Hf
|
syn
|
1.87 y
|
ε
|
172Lu
|
174Hf
|
0.162%
|
2×1015 y
|
α
|
170Yb
|
176Hf
|
5.206%
|
-
|
(α)
|
172Yb
|
177Hf
|
18.606%
|
-
|
(α)
|
173Yb
|
178Hf
|
27.297%
|
-
|
(α)
|
174Yb
|
178m3Hf
|
syn
|
31 y
|
IT
|
178Hf
|
179Hf
|
13.629%
|
-
|
(α)
|
175Yb
|
180Hf
|
35.1%
|
-
|
(α)
|
176Yb
|
182Hf
|
trace
|
8.9×106 y
|
β−
|
182Ta
| |
Decay modes in parentheses are predictit, but hae nae yet been observed |
| references |